Item Test Method Unit AR-1040 AR-1050 AR-1060
Hardness JIS K 6253 A point 40 50 60
Specific Gravity JIS K 7112 - 1.12 1.15 1.15
Melt Flow Rate ASTM D 1238
230℃ x 49.0N
g/10min 1 2 2
Tensile at Break JIS K 6251 MPa 4.6 6.1 7.2
300% Modulus JIS K 6251 MPa 3.3 3.8 5.4
Elongation JIS K 6251 % 420 510 450
Tear Strength JIS K 6252 kN/m 12 15 17
Resilience JIS K 6255 % 47 47 39
Taber abrasion Test JIS K 6264
H-22 x 9.8N x 1000 Cycle
mg 1029 718 550
Compression Set -
-
-
-
-
23℃ x 24hr JIS K 6262 % 10 10 12
70℃ x 24hr JIS K 6262 % 12 12 21
100℃ x 24hr JIS K 6262 % 23 25 26
Softening Temperature our method 97 100 128
Brittleness Temperature JIS K 6261 -50℃ or less
Weather resistance -
-
Mold Shrinkage our method % 0.4 / 3.1 0.3 / 2.8 0.5 / 2.3
Molding Method -
-
Injection / Extrusion
Drying -
-
unnecessary
Color - -
Black
※ The values shown in the table are representative ones and not guaranteed.