ARONKASEI CO., LTD.
| Item | Test Method | Unit | AR-1040 | AR-1050 | AR-1060 | |
|---|---|---|---|---|---|---|
| Characteristic | - | Standard | ||||
| Hardness | JIS K 6253 | typeA | point | 40 | 50 | 60 |
| Specific Gravity | JIS K 7112 | - | 1.12 | 1.15 | 1.15 | |
| Melt Flow Rate | ASTM D 1238 | 230℃×49N | g/10min | 1 | 2 | 2 |
| Tensile strength | JIS K 6251 | MPa | 4.6 | 6.1 | 7.2 | |
| 300%Modulus | 〃 | 〃 | 3.3 | 3.8 | 5.4 | |
| Elongation | 〃 | % | 420 | 510 | 450 | |
| Tear Strength | JIS K 6252 | kN/m | 12 | 15 | 17 | |
| Rebound resilience | JIS K 6255 | % | 47 | 47 | 39 | |
| Taber abrasion Test | JIS K 6264 | H22×9.8N×1000Cycle | mg | 1029 | 718 | 550 |
| Compression Set | JIS K 6262 | 23℃×24hr | % | 10 | 10 | 12 |
| 70℃×24hr | 〃 | 12 | 12 | 21 | ||
| 100℃×24hr | 〃 | 23 | 25 | 26 | ||
| Softening Temperature | our method ※1 | ℃ | 97 | 100 | 128 | |
| Brittleness Temperature | JIS K 7216 | 〃 | <-50 | |||
| Weather resistance | - | - | ◎ | |||
| Mold Shrinkage (Vertical/Flowing directions) |
our method ※2 | % | 0.4/3.1 | 0.3/2.8 | 0.5/2.3 | |
| Molding Method | - | - | Injection ・ Extrusion | |||
| Drying | - | - | unnecessary | |||
| Color | - | - | Black | |||
| Fusion strength | our method | PP | - | ○ | ○ | ○ |
| ABS | - | × | × | × | ||
| PC | - | × | × | × | ||
| PET | - | × | × | × | ||
| 6Ny(PA) | - | × | × | × | ||
| PBT | - | × | × | × | ||
| POM | - | × | × | × | ||
| PVC | - | × | × | × | ||
| Flame Retardance | UL-94 | - | HB | HB | HB | |
The values shown in the table are representative ones and not guaranteed.
The figures in the table are subject to change without notice.
Reproduction of this information without our consent is prohibited.
※1 Softening temperature measurement method: Vicat softening temperature (at temperature rise rate of 50℃/hour and load of 2.5N)was determined with a needle inserted by 1mm.
※2 Shrinkage：A film gate sheet (126mm x 126mm x 2mm)was formed (at mold temperature of 40℃ and cooling period of 40 seconds).
※3 This is a grade that is made to order and sold.