Colorable＆Low specific gravity grade VP series (ARVAS / TPV)

Colorable＆Low specific gravity grade VP series
(ARVAS / TPV)

Features

1. Low density, ideal for lightweight applications. (Specific gravity: 0.9 or less)
2. It can be colored, increasing the degree of design freedom.
3. We have a wide range of lineups, including grades with high rubber elasticity, semi-rigid grades (A60 to D45), and grades according to molding methods (injection, extrusion molding, etc.).
4. Excellent long-term compression set.

Download

Properties

ARONKASEI CO., LTD.

Item	Test Method		Unit	VP-A60NT	VP-A70NT	VP-A70ET	VP-A80ET	VP-A90ET	VP-D45ET	VP-D36HT
Item	Characteristic		-	Standard						High flow
Hardness	JIS K 6253	typeA	point	60	73	70	81	94	97	96
Hardness	JIS K 6253	typeD	〃	-	-	-	-	38	48	37
Specific Gravity	JIS K 7112		-	0.88	0.88	0.88	0.89	0.89	0.89	0.89
Melt Flow Rate	ASTM D 1238	230℃×49N	g/10min	1	0.2	1	1	2	2	84
Tensile strength	JIS K 6251		MPa	4.8	6.2	7.0	8.3	14.5	19.5	9.0
Elongation	〃		%	540	440	520	610	710	830	470
Tear Strength	JIS K 6252		kN/m	25	34	34	51	84	108	77
Rebound resilience	JIS K 6255		%	50	52	47	45	40	40	39
Taber abrasion Test	JIS K 6264	H22×9.8N×1000Cycle	mg	77	296	204	102	123	108	157
Compression Set	JIS K 6262	23℃×24hr	%	36	32	38	35	unmeasurable	unmeasurable	unmeasurable
		70℃×24hr	〃	40	36	40	48	59	58	75
		100℃×24hr	〃	43	31	41	47	66	68	79
Softening Temperature	our method ※1		℃	105	123	127	131	158	162	151
Brittleness Temperature	JIS K 7216		〃	<-60					-45	-40
Mold Shrinkage (Vertical/Flowing directions)	our method ※2		%	1.1/1.6	1.3/1.7	1.3/1.8	1.1/1.4	1.1/1.5	1.0/1.4	1.1/1.2
Molding Method	-		-	Injection ・ Extrusion						Injection
Drying	-		-	unnecessary
Color	-		-	Natural ・Black
Fusion strength	our method	PP	-	○	○	○	○	○	○	○
		ABS	-	×	×	×	×	×	×	×
		PC	-	×	×	×	×	×	×	×
		PET	-	×	×	×	×	×	×	×
		6Ny(PA)	-	×	×	×	×	×	×	×
		PBT	-	×	×	×	×	×	×	×
		POM	-	×	×	×	×	×	×	×

The values shown in the table are representative ones and not guaranteed.
The figures in the table are subject to change without notice.
Reproduction of this information without our consent is prohibited.
※1　Softening temperature measurement method: Vicat softening temperature (at temperature rise rate of 50℃/hour and load of 2.5N)was determined with a needle inserted by 1mm.
※2　Shrinkage：A film gate sheet (126mm x 126mm x 2mm)was formed (at mold temperature of 40℃ and cooling period of 40 seconds).
※3　This is a grade that is made to order and sold.